  • Zinc adhesion on galvanized wire surface and thickness of zinc layer


  • Post time: 06-04-23
  • Pay attention to safety in line collection and operation, others without the consent of the monitor, Ben have to get on the bus operation. The reels should be placed lightly, stacked firmly and neatly, not more than 5 reels. Direct contact with acid and alkali must be prohibited. When the acid fog exceeds the specified target of the state, measures should be taken to control it in time, otherwise production is not allowed.

  • In the rolling process, if the surface of the steel wire is rough, the relative friction coefficient of the steel wire and roll increases, the friction resistance increases, the steel wire elongation decreases, the width increases. In the production of weighted leather material is easy to wide, is because of its rough surface. On the contrary, the surface of the steel wire is smooth, because the friction resistance between the steel wire and the roll is small, it is easy to extend, and the width is small. Domestic steel wire in order to prevent rust, the surface coated with butter, such as butter removal is not clean, easy to slip when rolled flat, also affect its width.
  • D, coating adhesion; The zinc layer of the plating parts should be firmly combined with the base metal with sufficient adhesion strength, and will not fall off or bulge after the hammer test.

  • barbed

  • Production technology: Through the excellent low carbon steel rod drawing forming, pickling rust removal, high temperature annealing, hot dip galvanizing. Cooling and other 5 operation processes refined. Galvanized wire characteristics: good resistance and elasticity, strong corrosion resistance.

  • The most obvious difference in a short time is the cross section of this piece, hot dip galvanized barbed wire because of surface anticorrosion treatment, so there will be rust in the cross section of this piece, and stainless steel barbed wire because the internal raw materials and surface raw materials are consistent, so there is no such situation.


  • Post time: 09-05-22

  • Post time: 31-03-23
  • With the improvement of people’s living standards, now many families are raising some small pets, these small pets need a stable nest, pet cage has become a more important choice of people, each pet habits and living habits will choose to adapt to the cage.

  • When laying steel wire mesh, according to the laying method from the middle to both sides in turn. Wall plastering engineering use wire mesh material is generally two kinds: one is electroplating, the other is hot dip galvanized. The former has low cost and a wide range of use. The cost of hot-dip galvanized material is slightly higher than that of electroplating, and the cost is high and the life is good to prevent rust. Hot dip galvanizing is in the case of heating plating. After the zinc is melted into liquid form, the base metal is immersed in it so that the zinc interpenetrates with the base metal and binds so tightly that there are no other impurities or defects left in the process.

  • Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

  • metal

  • hot

  • Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.

  • No less than 5 disks should be extracted from each inspection lot for diameter error inspection. 1 point of steel wire should be extracted from each disk to measure steel wire diameter, and the actual diameter of steel wire at this point should be taken as the average value of the two vertical directions. The diameter error of cold-drawn low carbon steel wire should conform to the rules in the table below. The unqualified inspection batches shall be checked one by one, and the qualified batches can be used for engineering.

  • C, coating uniformity: galvanized layer is basically uniform with copper sulfate solution test etched five times without exposing iron.
  • In order to remove the photosynovium and oxide remaining on the surface of galvanized iron wire after drawing or heat treatment, it is necessary to do the surface treatment of galvanized steel wire before plating. The common surface of low carbon steel wire is the light synovium or oxide of animal or vegetable oil; Medium and high carbon steel in addition to contain animal or vegetable oil components.

  • 3. The structure of the dog cage should be reasonable

  • Post time: 31-10-22

  • Post time: 09-05-22
  • Even PVC coated barbed rope in ultra wet areas, will play an unexpected result.
  • 1. The diameter of raw materials and the thickness of the diameter have a direct impact;