floor mat anti skid

Blade thorn rope because the volume is relatively large so thorn rope factory is used to packaging treatment.

Small iron wire is very useful in our life, basically a lot of things will use iron wire, and iron wire can also be made into a lot of crafts, making ordinary iron wire become more aesthetic and artistic sense. Of course, the iron wire in the process of use, there will be rust, so galvanized black iron wire in the storage process, it is necessary to master the correct method.

Some customers may not immediately use the blade barbed rope when they buy it for retail and some are temporarily not used for site construction. At this time, customers need to follow up the characteristics of the blade barbed rope for storage. Because they are afraid of the rain, so there is no need to say more, and the surface of the packaging is more afraid of the sun, so it is not recommended to prevent the outside of the blade thorn rope will lead to the woven bag become lost effect, resulting in the exposure of the internal blade thorn rope affect the later use.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

Cold galvanized by electrolytic action to metal and other materials surface attached to a layer of metal film, so that the surface of the material uniform texture, anti-corrosion wear, appearance is more beautiful. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other “rough” workpiece long-term rust prevention.

2, the production and installation is simple and fast, the use of patented friction connection or special connection accessories for installation, greatly improve the installation efficiency.