Because there are many large livestock in pasture, and because of the large cost of development and easy to be destroyed by livestock, galvanized barbed rope is the best choice for enclosure. Pasture installation thorn rope is necessary,  wire mesh factory to introduce the role of pasture installation thorn rope。

Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.

In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.

Hot wire mesh in the building wall engineering mainly played the anti-crack effect, inside and outside the use of specifications are not the same. Hot dipped wire material choose low carbon wire, through automation welding precision machinery processing after forming, surface treatment by zinc immersion process, galvanized barbed wire surface smooth and tidy, uniform structure strong, the overall performance is good, even if the local cutting or under pressure will not loose phenomenon occurs, it is the iron mesh strong anticorrosion performance in one of the widely used net class.

The distance between the adjacent two thorn rope installation do not know whether you have noticed? Careful observation can find that its spacing is not the same, the thorn rope factory for customer consultation when asking the installation height of the reason.

In order to make the zinc content of steel wire stable in the future, and maintain its uniformity, as far as possible to reduce the zinc content, and effectively reduce zinc consumption to the actual work, the following measures are proposed by the wire factory:

The physical methods mainly include manual rust removal and mechanical rust removal, chemical rust removal is generally the use of pickling method, practical application, usually according to the appearance of the workpiece rust status and different post-treatment process, choose different rust removal methods, among which pickling rust cleaning is more commonly used. That is, the iron and steel workpiece with oxide skin or rust is etched in the acid lotion, mainly to remove the oxide or rust layer on the surface of the steel.

In daily life, what we can bend by hand is basically galvanized iron wire, not steel wire. It has a high zinc content, which ensures its good toughness and resilience, but also has ultra-high corrosion resistance, which can last for decades in outdoor environments. There are many practicability of galvanized iron wire, such as strong reliability, galvanized layer and iron together, form a special metallurgical structure, in the use and transportation process, can ensure that will not be mechanical damage.

The derusting steel parts are immersed in the melted zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to achieve the purpose of anti-corrosion. The surface of galvanized wire coating can see whether the quality of galvanized wire is good or not. If the strength of zinc attached to the wire is very poor, then this galvanized wire do not buy, because this galvanized wire must be poor galvanized wire.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

Many electrogalvanized wire diameter products are formed by wire drawing, wire drawing is a kind of processing technology, can make the product reach the required shape and meet the standard mechanical properties. Cold wire drawing is carried out at recrystallization temperature, hot wire drawing is carried out at crystallization temperature, warm wire drawing is drawn at higher than room temperature and lower than crystallization temperature. Cold drawing is a common drawing method.